Physical
Property*
|
ASTM
Method
|
||||
|
Hardness,
Shore A
|
-
|
80
|
90
|
93
|
95
|
|
Shore
D
|
-
|
-
|
-
|
-
|
50
|
|
Tensile,
psi (MPa)
|
D412
|
3600
(25)
|
4100
(28.3)
|
5400
(37)
|
5500
(37.9)
|
|
Elogation
At Break, %
|
D412
|
750
|
450
|
400
|
350
|
|
100%
Modulus, psi (MPa)
|
D412
|
560
(3.9)
|
1000
(6.9)
|
1800
(12.4)
|
2200
(15.2)
|
|
300%
Modulus, psi (MPa)
|
D412
|
800
(5.5)
|
1700
(11.7)
|
3100
(21.4)
|
4100
(28.3)
|
|
Split
Tear, lb./in. (kN/m)
|
D470
|
80
(14)
|
65
(11.4)
|
80
(14)
|
125
(21.9)
|
|
Die
C Tear, lb./in. (kN/m)
|
D624
|
320
(56)
|
370
(64.8)
|
430
(75)
|
500
(87.6)
|
|
Bashore
Rebound, %
|
D2632
|
55
|
50
|
45
|
42
|
| Compression Set (Method B) 22 Hours At 158°F (70°C), % |
D395
|
45
|
25
|
30
|
32
|
| Compressive Modulus, psi (MPa) | |||||
| Third Cycle |
D575
|
||||
|
5%
|
115
(0.8)
|
210
(1.4)
|
355
(2.5)
|
500
(3.4)
|
|
|
10%
|
190
(1.4)
|
350
(2.4)
|
590
(4.1)
|
840
(5.8)
|
|
|
15%
|
260
(1.8)
|
490
(3.4)
|
820
(5.7)
|
1200
(8.3)
|
|
|
20%
|
370
(2.6)
|
680
(4.7)
|
1130
(7.8)
|
1650
(11.4)
|
|
|
25%
|
520
(3.6)
|
940
(6.5)
|
1550
(10.7)
|
2100
(14.5)
|
|
| Brittle Temperature, °F (°C) |
D748
|
<-94(<-70)
|
<-94(<-70)
|
<-94(<-70)
|
<-94(<-70)
|
| Spcific Gravity |
D792
|
1.07
|
1.08
|
1.11
|
1.13
|
| Dynamics |
-
|
Very
good
|
Excellent
|
Excellent
|
Excellent
|
|
Source: Uniroyal Chemical ®
|
|||||
| There are many other materials available. Contact us for your Custom Formulation. | |||||
For Product Details of our high quality Urethane
Products, please
Click Here.
Go back to Engineering Assistance
|
|
|
|
|
|
UrethaneServices.com © Copyright 2020. All Rights Reserved. View the Applied Urethane Technology, Inc. Copyright Notice No website content can be duplicated without first obtaining our written permission. This web site was designed, and is being updated by Silverlining Web Graphics.