Physical Property*
|
ASTM Method
|
|
|
|
|
|
Hardness, Shore A
|
-
|
95
|
-
|
-
|
-
|
-
|
Shore D
|
-
|
50
|
60
|
65
|
70
|
74
|
Tensile, psi (MPa)
|
D412
|
5500 (37.9)
|
6700 (46.2)
|
7000 (48.3)
|
7000 (48.3)
|
7100 (48.9)
|
Elogation At Break, %
|
D412
|
350
|
290
|
260
|
250
|
230
|
100% Modulus, psi (MPa)
|
D412
|
2200 (15.2)
|
3600 (24.8)
|
4100 (28.3)
|
4500 (31.0)
|
5300 (36.5)
|
300% Modulus, psi (MPa)
|
D412
|
4100 (28.3)
|
-
|
-
|
-
|
-
|
Split Tear, lb./in. (kN/m)
|
D470
|
125 (21.9)
|
115 (20.1)
|
115 (20.1)
|
130 (22.8)
|
140 (24.5)
|
Die C Tear, lb./in. (kN/m)
|
D624
|
500 (87.6)
|
600 (105)
|
670 (117)
|
800 (140)
|
900 (158)
|
Bashore Rebound, %
|
D2632
|
42
|
40
|
40
|
-
|
-
|
Compression Set (Method B) 22 Hours At 158°F (70°C), % |
D395
|
32
|
28
|
29
|
-
|
-
|
Compressive Modulus, psi (MPa) |
|
|
|
|
|
|
Third Cycle |
D575
|
|
|
|
|
|
5%
|
|
500 (3.4)
|
1000 (6.9)
|
1310 (9.0)
|
1650 (11.4)
|
2150 (14.8)
|
10%
|
|
840 (5.8)
|
1650 (11.4)
|
2110 (14.5)
|
2600 (17.9)
|
3700 (25.5)
|
15%
|
|
1200 (8.3)
|
2300 (15.9)
|
2900 (20.0)
|
3400 (23.4)
|
4700 (32.4)
|
20%
|
|
1650 (11.4)
|
3100 (21.4)
|
3800 (26.2)
|
4200 (29.0)
|
6000 (41.4)
|
25%
|
|
2100 (14.5)
|
4000 (27.6)
|
4840 (33.4)
|
5200 (35.8)
|
7250 (50.0)
|
Brittle Temperature, °F (°C) |
D748
|
<-94(<-70)
|
<-94(<-70)
|
<-94(<-70)
|
<-94(<-70)
|
|
Spcific Gravity |
D792
|
1.13
|
1.16
|
1.17
|
1.18
|
1.20
|
Dynamics |
-
|
Excellent
|
Excellent
|
Excellent
|
Excellent
|
Excellent
|
Source: Uniroyal Chemical ®
|
|||||
There are many other materials available. Contact us for your Custom Formulation. |
Go back to Engineering Assistance
|
|
|
|
|
|
UrethaneServices.com © Copyright 2020. All Rights Reserved. View the Applied Urethane Technology, Inc. Copyright Notice No website content can be duplicated without first obtaining our written permission. This web site was designed, and is being updated by Silverlining Web Graphics.